The compound mirror finish aluminum sheet and compound matt finish aluminum sheet are our company's primary product. The above-mentioned products already trade mark registration and make its reputation locally and internationally through our research and development effort from time to time .These products is one type of the high reflective vacuum zincification compound material ,it primarily used for high efficiency fluorescent mirror louver .We adopt the most advance high vacuum continuous /accumulate sinks and compound techniques to process the products and giving up the precise work and high technical manufacture procedures .As the result ,the products having high reflective ,high alternative lighting advantage function .
Technique information
    1. The GS ( 45C )mirror reflective rate larger than 80%,and if compare with others material :
    High reflective vacuum zincification compound material 88%
    Stainless steel mirror reflector 44%
    Aluminium sheet anode oxidize mirror reflector 30%
    White paint mirror reflector 3.8%
    2. Material stand for ageing in sun barking ;
    Outdoor 2years
    Indoor 10years
    3. Mechanical function :
    ( A ) :ratio of anti-pulling /tearing ( vertically & horizontally )>160Mpa
    ( B ) ratio of anti-broken /crack (vertically & horizontally )>70%
    ( C ) ratio of heat bulginess ( vertically & horizontally )<3%
    ( D ) Melting point > 238 oC
    4. Strength of aluminum sheet and anodized adhesive (with comply to GB 2794-81-84)requirement
    ( 1 ):preliminary adhesive strength 23±2oC>No. 3 steel ball
    ( 2 )Special strong adhesive strength 23±2oC 1kg 24h
    ( 3 )180 C removal force 25mm 30mm /min 0.9 kg
    ( 4 ) evenly of the adhesive layer with no bubble.
    5. Strength of rubbing :
we use 5 x 6 cm net wood with 8 layer of gauses to press 0.3kg /cm 2,glide speed 120 cm per minute, vertically and horizontally rubbed for five times in order to make the ratio of reflection unchanged and minimize the crease .
    6. Material bending dimension ,machine casting into shape to make lighting products and would not have breaking ,cracking and goffer occurred .
    Make use of the high reflective vacuum zincification compound material will therefore result to special function of 80%more brightening the reflective rate and also result to 80%more reflective rate to infrared rays and therefore ,the material can used widely in the field of lighting industry like ,mirror reflector for instance ,and also used in heat preservation (cool room ,refrigerator)as well as other places like hotel ,shopping center ,exhibition hall ,office ,cabin etc. ,it’s not merely increase the lighting quality but also obviously save the energy .Take YG 2-2x 40W and 2x16W fluorescent for example ,it will either brightening from 25% to 30% ,and will result to energy saving and luxury feel of the lighting if compare in using normal white painted mirror reflector or aluminum sheet anode oxidize mirror reflector .